Concrete Failure Analysis and Forensic Investigations

Concrete is a widely used precast element and used in-situ in walls, floors, foundations and structural components. There are rules in Eurocode 2 for use of concrete with regards to strength, durability, fire resistance and movement tolerances. When installations fail, a forensic examination is required to understand the failure mechanism in order to: detail methods of repair, understand the consequences of the failure, or ultimately, to be able to define culpability.

Lucideon has a number of techniques available for forensic/failure analysis which can be split into two categories; site investigation followed by laboratory analysis.

Concrete Failure Analysis

 

Site investigation

An initial desk study will be followed by a visual site inspection to assess the failure mode. Depending on the apparent failure, a programme of intrusive and non-intrusive sampling can be carried out:

Intrusive coring of samples to establish:

  • depth of cover to rebar
  • construction of slab/column/beam
  • presence of honeycombing
  • moisture content and density
  • depth of foundation

Non-intrusive investigation:

  • mapping of rebars using Hilti Ferroscan
  • presence of voids using Ground Penetrating Radar (GPR)
  • estimated compressive strength using Schmidt Hammer or Windsor Pin
  • presence of movement joints
  • drop hammer testing of screeds to establish strength
  • slip/skid testing of surface
  • half cell potential.

Laboratory analysis

  • compressive strength*
  • mix proportions including identification of additives*
  • petrographic analysis*
  • sulfate content*
  • chloride content*
  • depth of carbonation
  • alkali silica reaction
  • presence of High Alumina Cement (HAC)*

Lucideon is a UKAS accredited test laboratory for many tests to BS 1881 and BS EN 12390, including the ones marked with an *.

 

Petrographic analysis

Petrographic analysis is a diagnostic tool for examining failures in concrete.

Once onsite, we can carry out an initial visual examination of the area in order to ascertain possible causes of the problem and to determine the best position for taking samples. Our engineers can take core samples and return them to the laboratory where thin sections will be prepared for examination using Scanning Electron Microscopy (SEM) and Polarized Light Microscopy (PLM).

Petrographic analysis is carried out in accordance with both European and American standards: BS 1881-211:2016, ASTM C295, ASTM C856 and ASTM C457.

Benefits of petrographic examination include:

  • determining the present condition of previously placed concrete so that the decision to re-use or replace can be decided
  • establishing the root cause of surface scaling, spalling, aggregate pop-outs and abrasion
  • defining cracks by type and uncovering crack mechanisms
  • explaining causes of concrete degradation; primary mechanisms are:
    • alkali-silica reaction (ASR)
    • alkali-carbonate reaction (ACR)
    • sulfate attack
  • effects of chemical attack (including chlorides)
  • assessing the entrained air content
  • establishing the water/cement ratio
  • determining the density, absorption and volume of permeable voids (as defined in ASTM C642)
  • revealing the root cause(s) of low compressive strength with key milestones at 7, 28 and 56 days
  • comparing hardened concrete to known mix designs
  • assessing fire damage

Forensic analysis can be supplemented by additional techniques which also include, but are not limited to chemical analysis, SEM and X-Ray Diffraction (XRD).

White Papers

Concreting Process
The Concreting Process and Petrographic Examination

This white paper provides a broad overview of the concreting process and discusses common deficiencies and degradation mechanisms in hardened concrete structures that require petrographic examination

Digital Image Correlation
The Use of Digital Image Correlation in Masonry Research

Digital Image Correlation is a technique that can deliver video footage of the strain development on the surface of a material due to loading or other actions

Offsite Construction
Offsite Construction: The Relevance of Full Scale Testing

The purpose of this paper is to show some examples where the results from whole building tests have demonstrated distinct improvements in performance

Case Studies

Hammersmith Flyover
Fryssinet and the Restoration of the Hammersmith Flyover

Testing provided evidence that the strength requirements of the UHPFRC were met at each stage of the flyover restoration process

Cracked Concrete Floor
Warehouse Floor Evaluation for Falliance

Analysis of concrete and screed identified that the flooring materials specified were not used and lower-cost alternatives were sourced

Precast Concrete Panels
Precast Concrete Modular Housing System

Testing and consultancy enabled third party insurance and building control sign-offs